Ceramic foam air filters with three‐dimensional (3D) porous structures and high surface areas were
coated with mesoporous TiO2 thin films by the reverse micellar method. The mesoporous TiO2 thin
films efficiently photocatalytically degraded nitrogen oxide (NO). More than 92.5% of NO was degraded
in a single pass for air filter samples containing different pore densities. The 3D porous
structure of the ceramic air filters enhanced flow turbulence and mixing. This provided the catalytic
system with excellent gas‐dynamic properties, and sufficient contact between the reactant gas and
catalyst surface. The higher pore density of the ceramic foam filters resulted in a higher photocatalytic
rate. More adsorption sites for water vapor and the reactant and product gases improved the
photocatalytic activity. The porous ceramic air filters coated with mesoporous TiO2 had large surface
areas, and thus high photocatalytic activity. This overcame the common disadvantages associated
with using powdered TiO2 photocatalysts on substrates. The 3D porous ceramic foam filters
coated with mesoporous TiO2 thin films exhibited a higher photocatalytic degradation rate of NO in
air than the same thin film deposited on flat ceramic tiles. No deactivation was observed. A consistently
high NO degradation rate was obtained between reaction cycles for the TiO2‐coated 3D porous
ceramic filters.
0/5000
From: -
To: -
Results (Malay) 1: [Copy]
Copied!
Penapis seramik buih udara dengan struktur berliang three‐dimensional (3D) dan kawasan-kawasan permukaan yang tinggi telahdisalut dengan mesoporous filem nipis TiO2 melalui kaedah micellar belakang. Mesoporous TiO2 nipisfilem dengan cekap photocatalytically miskin nitrogen oksida (NO). Lebih daripada 92.5% tidak miskindalam Pas yang tunggal untuk sampel penapis udara yang mengandungi berbeza liang kepadatan. 3D berliangstruktur penapis seramik udara dalam mempertingkatkan aliran pergolakan dan mencampurkan. Ini disediakan di perangsangsistem dengan sifat-sifat gas‐dynamic yang sangat baik, dan kenalan yang mencukupi antara reactant gas danpermukaan pemangkin. Ketumpatan tinggi liang penapis seramik buih mengakibatkan photocatalytic yang lebih tinggikadar. Memperbaiki Laman penjerapan lebih banyak wap air dan gas-gas reactant dan produk yangaktiviti photocatalytic. Penapis Penyaman seramik berliang yang disalut dengan mesoporous TiO2 mempunyai permukaan yang besarbidang, dan dengan itu aktiviti photocatalytic tinggi. Ini mengatasi kelemahan umum yang berkaitandengan menggunakan tepung photocatalysts TiO2 pada substrat. Penapis 3D buih seramik berliangdisalut dengan mesoporous TiO2 filem nipis mempamerkan photocatalytic penurunan kadar yang lebih tinggi tidak didingin daripada filem nipis yang sama dimasukkan ke dalam jubin seramik rata. Penyahaktifan tidak diperhatikan. A secara konsistentinggi kadar kemerosotan TIDAK diperolehi antara reaksi kitaran untuk 3D TiO2‐coated berliangpenapis seramik.
Being translated, please wait..
Results (Malay) 2:[Copy]
Copied!
Seramik penapis buih udara dengan tiga dimensi (3D) struktur berliang dan kawasan permukaan yang tinggi telah
disalut dengan filem nipis TiO2 mesoporous dengan kaedah misel terbalik. The mesoporous nipis TiO2
filem cekap photocatalytically dihina nitrogen oksida (NO). Lebih daripada 92.5% daripada NO telah dihina
dalam satu laluan untuk sampel penapis udara yang mengandungi kepadatan liang yang berbeza. 3D berliang
struktur penapis udara seramik dipertingkatkan pergolakan aliran dan pencampuran. Ini menyediakan pemangkin
sistem dengan ciri-ciri gas-dinamik yang sangat baik, dan kenalan yang mencukupi antara gas bahan tindak balas dan
permukaan pemangkin. Ketumpatan liang yang lebih tinggi daripada penapis buih seramik menyebabkan photocatalytic yang lebih tinggi
kadar. Lebih banyak tapak penjerapan wap air dan bahan tindak balas dan produk gas meningkatkan
aktiviti photocatalytic. Penapis udara seramik berliang bersalut dengan TiO2 mesoporous mempunyai permukaan yang besar
kawasan, dan aktiviti photocatalytic itu tinggi. Ini mengatasi kelemahan yang biasa dikaitkan
dengan menggunakan photocatalysts TiO2 serbuk pada substrat. 3D berliang penapis buih seramik
bersalut dengan filem nipis TiO2 mesoporous dipamerkan Kadar kemerosotan photocatalytic yang lebih tinggi NO dalam
udara daripada filem nipis yang sama disimpan di jubin seramik rata. Tiada penyahaktifan diperhatikan. A konsisten
kadar degradasi NO tinggi telah diperolehi antara kitaran tindak balas bagi 3D berliang TiO2 bersalut
penapis seramik.
Being translated, please wait..
 
Other languages
The translation tool support: Afrikaans, Albanian, Amharic, Arabic, Armenian, Azerbaijani, Basque, Belarusian, Bengali, Bosnian, Bulgarian, Catalan, Cebuano, Chichewa, Chinese, Chinese Traditional, Corsican, Croatian, Czech, Danish, Detect language, Dutch, English, Esperanto, Estonian, Filipino, Finnish, French, Frisian, Galician, Georgian, German, Greek, Gujarati, Haitian Creole, Hausa, Hawaiian, Hebrew, Hindi, Hmong, Hungarian, Icelandic, Igbo, Indonesian, Irish, Italian, Japanese, Javanese, Kannada, Kazakh, Khmer, Kinyarwanda, Klingon, Korean, Kurdish (Kurmanji), Kyrgyz, Lao, Latin, Latvian, Lithuanian, Luxembourgish, Macedonian, Malagasy, Malay, Malayalam, Maltese, Maori, Marathi, Mongolian, Myanmar (Burmese), Nepali, Norwegian, Odia (Oriya), Pashto, Persian, Polish, Portuguese, Punjabi, Romanian, Russian, Samoan, Scots Gaelic, Serbian, Sesotho, Shona, Sindhi, Sinhala, Slovak, Slovenian, Somali, Spanish, Sundanese, Swahili, Swedish, Tajik, Tamil, Tatar, Telugu, Thai, Turkish, Turkmen, Ukrainian, Urdu, Uyghur, Uzbek, Vietnamese, Welsh, Xhosa, Yiddish, Yoruba, Zulu, Language translation.

Copyright ©2025 I Love Translation. All reserved.

E-mail: