A industrial solid waste from the p

A industrial solid waste from the process of precision casting by lost-ax was used and evaluated for the production of ceramic filters. PU sponges(9.8ppi)impregnated with a stable suspension were
successfully fired at 1550 1C/2 h so that filters wellr eproduced (9.5ppi),and mechanically stronger
(1.0MPa) were obtained.The produced filters tested in industrial scale showed very good performances
with good filtering efficiency (1.7kg/s)for liquid cast iron.

Results (Malay) 1:

A sisa pepejal perindustrian dari proses persis lakonan oleh ax hilang digunakan dan dinilai untuk pengeluaran penapis seramik. PU SPAN (9.8ppi) kelambu dengan penggantungan stabil telahberjaya dipecat pada 1550 1C/2 j jadi yang menapis eproduced wellr (9.5ppi), dan mekanikal kuat(1.0MPa) telah diperolehi. Penapis dihasilkan diuji dalam skala industri yang menunjukkan prestasi yang sangat baikdengan baik penapisan kecekapan (1.7 kg/s) bagi besi Tuang cecair.

Results (Malay) 2:

A sisa pepejal perindustrian daripada proses pemutus ketepatan oleh hilang-kapak telah digunakan dan dinilai untuk pengeluaran penapis seramik. PU span (9.8ppi) berubat dengan penggantungan yang stabil telah
berjaya dipecat pada 1550 1C / 2 h supaya penapis wellr eproduced (9.5ppi), dan mekanikal kuat
(1.0MPa) adalah obtained.The dihasilkan penapis diuji dalam skala industri menunjukkan sangat baik persembahan
dengan kecekapan penapisan yang baik (1.7 kg / s) untuk cecair besi tuang.